Aguaje seed (a typical Amazonian forest fruit) was used as a precursor material for the production of activated carbon using phosphoric acid as activating agent in two different concentrations: 0,75 and 1,0 gH3PO4/gPrecursor. The physicochemical properties were studied by N2 sorption measurements, Boehm titration, scanning electron microscopy and energydispersive X-ray spectroscopy. Activated carbons were used in the adsorption of three heavy metals: lead, cadmium and chromium. The maximum adsorption capacity was achieved using activated carbon AG0,75_600 in a solution with a pH greater than 4 and the values obtained were in the following order: lead (74,8 mg g-1), cadmium (26,5 mg g-1), chromium (18,8 mg g-1). The most important factors influencing the adsorption process were the pH of the solution, the porous structure and surface acidity of the activated carbon.

La semilla de aguaje (fruto típico de la selva amazónica) fue empleada como un material precursor para la preparación de carbón activado usando ácido fosfórico como agente activante en dos concentraciones diferentes: 0,75 y 1,0 gH3PO4/gPrecursor. Las propiedades fisicoquímicas se estudiaron mediante mediciones de adsorción de nitrógeno, titulación Boehm, microscopía electrónica de barrido y espectroscopía de rayos X por energía dispersiva. Los carbones activados se utilizaron en la adsorción de tres metales pesados: plomo, cadmio y cromo. La máxima capacidad de adsorción se logró utilizando el carbón activado AG0,75_600 con soluciones con un pH mayor a 4; los valores obtenidos estaban en el siguiente orden: plomo (74,8 mg g-1) , cadmio (26,5 mg g-1), cromo (18,8 mg g-1). Los factores más importantes que influyen en el proceso de adsorción fueron el pH de la solución, la estructura porosa y la acidez superficial del carbón activado.