MgCaSi 2 O 6 polycrystal was synthesized by the devitrification method. The dosimetric characteristics by TL of this prepared polycrystal was investigated. This material exhibits TL peaks at 115, 160, 210, 260 and 280 °C. The dosimetric peak occurs at 260 °C with a well defined glow curve structure. This peak shows a linear dose response. Electron paramagnetic resonance (EPR) studies have been carried out to identify the defect centers responsible for the TL peaks. Two defect centers in the region of g = 2.0 are found. One of the centers (center I) with a g factor equal to 2.0085 is identified as O − -ion and relates with the observed high temperature 250 and 300 °C TL peaks. Additional defect centers with g = 2.0012 (center II) and 1.982 (center III) are due to F + -centers (electron trapped at an oxygen vacancy). Center II and III correlate with the TL peaks at 160 °C and 106 °C, respectively.