The present work addresses the systematic evaluation of the influence of the incorporation of dopant species (Ca+2, Ag+1) on the structural and functional properties of bismuth ferrite (BFO) nanocrystalline powders and films. Pure and doped BFO powders and thin films were synthesized by a modified sol-gel method. The concentration of the doping species varied from 0 up to 7 at %. The development of the host BFO structure was confirmed by XRD analyses of samples annealed at 700°C for one hour in air and nitrogen atmosphere. Thicknesses of films varied between 80 and 200 nm, depending on the concentration of Ca+2 species. Doped BFO exhibited a magnetic behavior that turned from paramagnetic into ferrimagnetic with the increase of Ca+2 concentrations.